| Specification |
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Pressing Methord;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate;
Product Name: Advanced Alumina-Carbon FT160 Ladle Slide Gate PLA;
Al2O3: 85% Min;
Apparent Porosity: 15%;
Bulk Density: 3GM./Cc Min;
C.C.S: 100MPa Min;
Application: Steel Mill Ladle;
Mould: According to The Customer's Request;
Function: Steel Metal Molten Flow Control;
Drawing: Customized;
Chemical Physical Analysis: Customized;
Sample Order: Acceptable;
Service Life: 4-8 Heats;
Main Material: Tabular Alumina, Carbonaceous Material;
Zirconia: Can Be Added;
Type: Alumina Carbon Refractory;
|
Classification: Cordierite, Mullite;
Feature: Long Time Materials;
Production Process: Sintering Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Customerised;
Al2O3: 48%-85%;
Fe2o3: 1.5-3.0%;
Bulk Density: 2.15-2.80 g/cm3;
Apparent Porosity: 16-24;
Certifiacte: ISO9001, CE, etc;
Cold Crushing Strength: 30-100 MPa;
Working Temperature: 1200~1700ºC;
Application: Industrial Furnace;
Thermal Shock Resistance: Excellent;
Usage: Ceramic Furnace;
Refractoriness Under Load (0.2MPa): 1350-1700 ºC;
Color: Yellow White;
Size Control: Accurate;
Production Time: 15-30 Days;
Testing Laboratory: Support;
|
Classification: Cordierite, Mullite;
Feature: Long Time Materials;
Production Process: Sintering Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Customerised;
Al2O3: 48%-85%;
Fe2o3: 1.5-3.0%;
Bulk Density: 2.15-2.80 g/cm3;
Apparent Porosity: 16-24;
Certifiacte: ISO9001, CE, etc;
Cold Crushing Strength: 30-100 MPa;
Working Temperature: 1200~1700℃;
Application: Industrial Furnace;
Thermal Shock Resistance: Excellent;
Usage: Ceramic Furnace;
Refractoriness Under Load (0.2MPa): 1350-1700 ℃;
Color: Yellow White;
Size Control: Accurate;
Production Time: 15-30 Days;
Testing Laboratory: Support;
|
Classification: Cordierite, Mullite;
Feature: Long Time Materials;
Production Process: Sintering Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Customerised;
Al2O3: 48%-85%;
Fe2o3: 1.5-3.0%;
Bulk Density: 2.15-2.80 g/cm3;
Apparent Porosity: 16-24;
Certifiacte: ISO9001, CE, etc;
Cold Crushing Strength: 30-100 MPa;
Working Temperature: 1200~1700℃;
Application: Industrial Furnace;
Thermal Shock Resistance: Excellent;
Usage: Ceramic Furnace;
Refractoriness Under Load (0.2MPa): 1350-1700 ℃;
Color: Yellow White;
Size Control: Accurate;
Production Time: 15-30 Days;
Testing Laboratory: Support;
|
Classification: Silicon Carbide (Sic);
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials;
Production Process: Sintering Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Pipe;
Sic Content (%): 90-99%;
Raw Material: Silicon Carbide (Sic);
Bulk Density: 2.7 g/cm3;
Apparent Porosity: 5~18%;
Certifiacte: ISO9001, CE, etc;
Feature 2: High Hardness, High Thermal Shoc;
Working Temperature: 1200~1700℃;
Application: Industrial Furnace;
Thermal Shock Resistance: Excellent;
Refractoriness: 1500-1800 ℃;
Refractoriness Under Load (0.2MPa): 1350-1700 ℃;
Color: Blank, Grey;
Size Control: Accurate;
Production Time: 15-30 Days;
Testing Laboratory: Support;
|