| Specification |
Feature: High Purity;
Manufacturing Technique: Artificial Graphite;
Compress Strength: 80-100 MPa;
Flexure Strength: 30-60 MPa;
Carbon Content: 99.9%;
Work Temperature: >3000℃;
|
Application Area: Automobile Industry, Electronic Industry, Food Industry, Mould Of Plastics;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: Pressing And Sintering;
Resistivity: 9~12 Micro Ohm.M;
Clearance: 12%;
Apply: Exothermic Melting Thermite Welding;
Block Density: 1.85g/Cc Min;
Compression Strength: 85MPa Min;
Model: Yxgm150;
Material: High Pure High Density Graphite;
Surface: Polised Mirror Surface;
Special Treatment: Pyrolytic Carbon Coating Available at Request;
Advantage: Anti-Abrasion, Long Service Life;
Flexural Strength: 40 MPa Min;
Compressive Strength: 85 MPa Min;
Ash Content: 0.1% Max;
Density: 1.73G/Cm³-2.0 G/Cm³;
|
Application Area: Automobile Industry, Electronic Industry, Food Industry, Mould Of Plastics;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: Pressing And Sintering;
Resistivity: 9~12 Micro Ohm.M;
Clearance: 12%;
Apply: Anti-Abrasion, Long Service Life;
Block Density: 1.85g/Cc Min;
Compression Strength: 85MPa Min;
Model: Yxgm150;
Material: High Pure High Density Graphite;
Surface: Polised Mirror Surface;
Special Treatment: Pyrolytic Carbon Coating Available at Request;
Advantage: Anti-Abrasion, Long Service Life;
Flexural Strength: 40 MPa Min;
Compressive Strength: 85 MPa Min;
Ash Content: 0.1% Max;
Density: 1.73G/Cm³-2.0 G/Cm³;
|
Application Area: Automobile Industry, Electronic Industry;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: 3D Printing Method;
Material: High Purity Graphite;
Advantages: High Temperature Resistance/ Acid Resistance/ Alka;
Application: Metal Melting/Refining Furnace;
Storage Conditions: Should Be Stocked in The Dry Situation;
Type: Graphite Mold;
Carbon Content: High-Carbon;
Grade: Industrial Grade;
Crystal Morphology: Compact Crystalline Graphite;
Composition: Graphite;
|
Application Area: Automobile Industry, Electronic Industry, Food Industry, Mould Of Plastics;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: Pressing And Sintering;
Resistivity: 9~12 Micro Ohm.M;
Clearance: 12%;
Apply: Anti-Abrasion, Long Service Life;
Block Density: 1.85g/Cc Min;
Compression Strength: 85MPa Min;
Model: Yxgm150;
Material: High Pure High Density Graphite;
Surface: Polised Mirror Surface;
Special Treatment: Pyrolytic Carbon Coating Available at Request;
Advantage: Anti-Abrasion, Long Service Life;
Flexural Strength: 40 MPa Min;
Compressive Strength: 85 MPa Min;
Ash Content: 0.1% Max;
Density: 1.73G/Cm³;
|